Sodium Chloride
Crystal properties |
||
Crystal Type |
cubic |
|
Transmission Range |
0.21 ... 26 µm |
|
Refractive Index |
1.49980 @ 9,5 µm |
|
Reflective Loss |
7.5 % @ 10.0 µm |
|
Reststrahlen |
50.1 µm |
|
Density. |
2.165 g/cm3 |
|
Melting Point |
801 °C |
|
Molecular Weight |
58.443 |
|
Thermal Conductivity |
6.49 W/(m K) |
|
Specific Heat |
854 J/(kg K) |
|
Thermal Expansion. |
44×10–6 / K @ –50...200 °C |
|
Hardness (Knoop) |
15.2 <110> |
|
Young’s Modulus |
39.98 GPa |
|
Shear Modulus |
12.61 GPa |
|
Bulk Modulus |
24.42 GPa |
|
Rupture Modulus |
2.38 Mpa |
|
Elastic Coefficient |
C11 = 48.7 / C12 = 12.6 / C44 = 12.75 GPa |
|
Dielectric Constant |
5.9 @ 25 °C, f = 100 Hz...25 GHz |
|
Solubility in Water |
35.7 g / 100 g @ 0 °C |
|
Cleavage Planes |
(100) |
|
Standard Diameter |
180 mm |
|
Application |
material for IR optic, CO2 laser windows |
|
Remarks |
soluble in glycerol, slightly soluble in alcohol and aquos ammonia, insoluble in HCl |
|
![]() |
||
![]() |