Barium Titanate
BaTiO3
|
Chemical name
Barium Titanate |
|
Chemical formula
BaTiO3 |
|
Melting point [°C]
1625 |
|
Crystal system
tetragonal |
|
Crystal Class
4/m (10 °C < T < 132 °C) |
|
Unit cell
a [Å]:3.99 b [Å]:3.99 c [Å]:4.04 (at 26 °C) |
|
Molecular weight [g/mol]
233.19 |
|
Mohs hardness
4.5 |
|
Density [g/cm3]
6.08 (at 25 °C) |
|
Refractive Index
n0=2.4912 (515 nm), 2.4160 (633 nm), 2.3681 (800 nm); ne=2.4247 (515 nm), 2.3630 (633 nm), 2.3235 (800 nm) |
|
Piezoelectric crystals
|
|
Termal conductivity [W/m/K]
6 (300 K) |
|
Thermal expansation coefficient [(10^(-5))/K]
15.7 || ?a; 6.2 || ?c |
|
Specific heat [J/(kg*K)]
0.527 (300 K) |
|
Crystal growth method
Top seeded solution growth (TSSG) |
|
Transmission range
0.43 - 6.30 μm |
|
Orientation
(100), (110), (001), (111) |
|
Electro optic coefficients
rT13 = 8±2 pm/V; rT33 = 105±10 pm/V; rT42 = 1300±100 pm/V |
|
Reflectivity of SPPC (at 0 deg. Cut)
40-60% (PureBaTiO3) at 515 nm; 50-80% (Ce:BaTiO3) at 633 nm; 40-60% (PureBaTiO3) at 633 nm |
|
Two wave mixing coupling constant
10-40 cm^(-1) |
|
Absorption loss [cm^(-1)]
0.285 (at 515 nm); 0.108 (at 633 nm); 0.033 (at 800 nm) |
|
Wavelength range for photo refractive effect
visible range for undoped BTO; 480-780 nm for Ce:BTO; 720-1060 nm for Rh:BTO |
|
Specifications |
|
Standard size [mm]
10x10; 10x5, 10x3, 5x5 |
|
Thickness
0.5, 1.0 mm |
|
Polishing
one or two side polished |
|
Bulk
5x5x5 mm; 4x4x4 mm; 3x3x3 mm; 0° or 45° cut, 2 - 6 faces polished |
|
Orientation accuracy
± 0.5 deg. |